Unit | Piece | |
---|
Specifications | - Can also be applied as a thick layer
- Fast drying
- Active corrosion protection (zinc phosphate)
| |
---|
Areas of application | Suitable for iron and steel | |
---|
Properties | - Can be repainted with 1- and 2-component varnishes
- Substrate: Kramp primer (layer thickness: 50 - 60 µm)
- Without the final covering layer, outdoor storage is possible for a maximum of 5 days
- High filling
- For electrostatic processing
- Thermal resistance: permanent load 120 °C, short-term load 150 °C
- Dry matter: 65-70%
- Limit viscosity (DIN 53 211): thixotropic
- Specific gravity (DIN 51 757): 1.4 - 1.5 kg/l
- Degree of gloss (DIN 67 530): 10 - 20%/60° (matt)
- It does not contain chromium and lead
- Adhesion (DIN 53 151): iron, steel: class 0 (very good)
| |
---|
Technical information | - Processing conditions: from + 10 °C and up to 80 % relative humidity
- Preparation of the substrate: The object to be treated must be thoroughly cleaned, degreased and, if necessary, sanded
- Dust-free drying: after 15 - 20 minutes (at 20 °C)
- Non-stick after 45 - 60 minutes (at 20 °C)
- Non-stick after 4-5 hours (at 20 °C)
- Final hardness after 3-4 days (at 20 °C)
- Using Kramp's quick-setting thinner can reduce drying times
- At lower temperatures, the drying time is prolonged
| |
---|
Benefits | - High coverage
- Saving time
- It ensures a long service life
| |
---|
Brand color | n/a | |
---|
Basic color | White | |
---|
Designed for the material | Metal | |
---|
Category | Primer | |
---|
Dust drying time | 30-60 min | |
---|
Type of packaging | Spray |
---|